供应 PA66日本东丽 CM3004G-15 加纤15%增强 含卤阻燃
¥32.60/kg
价 格 ¥27.50/kg
所 在 地 广东
发布日期 2019-06-12 14:21:26
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||
基本性能 | 吸水率 | 23℃,24hr | ASTM D-570 |
| % | ||
吸水率 | 23℃ | ASTM D-570 |
| % | |||
物理性能 | 比重 | ASTM D-792 |
| ||||
机械性能 | 断裂伸长率 | -40℃ | ASTM D-638 |
| % | ||
弯曲模量 | 23℃ | ASTM D-790 |
| GPa | |||
IZOD缺口冲击强度 | -40℃ | ASTM D-256 |
| J/m | |||
弯曲模量 | 80℃ | ASTM D-790 |
| GPa | |||
拉伸屈服强度 | 23℃ | ASTM D-638 |
| MPa | |||
弯曲模量 | -40℃ | ASTM D-790 |
| GPa | |||
弯曲强度 | 23℃ | ASTM D-790 |
| MPa | |||
断裂伸长率 | 23℃ | ASTM D-638 |
| % | |||
拉伸屈服强度 | 80℃ | ASTM D-638 |
| MPa | |||
IZOD无缺口冲击强度 | 23℃ | ASTM D-256 |
| KJ/m2 | |||
弯曲强度 | -40℃ | ASTM D-790 |
| MPa | |||
IZOD缺口冲击强度 | 23℃ | ASTM D-256 |
| J/m | |||
抗压强度 | -40℃ | ASTM D-695 |
| MPa | |||
抗压强度 | 23℃ | ASTM D-695 |
| MPa | |||
抗压强度 | 80℃ | ASTM D-695 |
| MPa | |||
剪切强度 | 23℃ | ASTM D-732 |
| MPa | |||
断裂伸长率 | 80℃ | ASTM D-638 |
| % | |||
弯曲强度 | 80℃ | ASTM D-790 |
| MPa | |||
洛氏硬度 | 23℃ | ASTM D-785 |
| R Scale | |||
IZOD无缺口冲击强度 | -40℃ | ASTM D-256 |
| KJ/m2 | |||
拉伸屈服强度 | -40℃ | ASTM D-638 |
| MPa | |||
热性能 | 热导率 |
| W/m℃ | ||||
线性热膨胀系数 | ASTM D-696 |
| 10-5/℃ | ||||
比热 |
| J/p℃ | |||||
熔点 | DSC |
| ℃ | ||||
热变形温度 | 0.46MPa | ASTM D-648 |
| ℃ | |||
热变形温度 | 1.86MPa | ASTM D-648 |
|
供应 PA66日本东丽 CM3004G-15 加纤15%增强 含卤阻燃
¥32.60/kg
供应PC日本三菱 GSH2010LR 加纤 抗冲 抗紫外线 阻燃
¥25.60/kg
供应 PA6/德国朗盛/BKV330H2.0 加纤33%玻纤增强 热稳定
¥32.00/kg
供应 PA66荷兰DSM/NY-3/MI/30 BK 加纤30增强 黑色
¥28.00/kg
供应PA6 日本东丽 CM1011G-45 加纤45%玻纤增强尼龙
¥27.50/kg
供应 PA6德国朗盛 BKV30H2.0 加纤30%增强 热稳定 本色
¥32.10/kg
供应 PA6德国朗盛 BKV215H2.0 加纤15%玻纤增强 热稳定
¥28.60/kg
免责声明:以上展示的"供应商PA6 日本东丽 CM1011G-45 加纤45%玻纤增强尼龙"信息由东莞市柏又伦塑料科技有限公司自行提供,内容的真实性、准确性和合法性由发布企业负责,朵拉利品网对此不承担责任。